Polymaker PC-ABS

Polymaker™ PC-ABS

Polymaker™ PC-ABS is a PC/ABS polymer blend which offers excellent toughness and heat resistance while displaying good surface finish and good compatibility with metal plating.


Excellent Toughness - Polymaker™ PC-ABS offers best in class toughness while combining the heat resistance of PC with the flexibility of ABS. An ideal choice for engineering and industrial applications, Polymaker™ PC-ABS displays a synergic effect resulting in superior impact resistance when compared to regular PC or ABS filaments.

Heat Resistant - Polymaker™ PC-ABS offers better heat resistance than a wide variety of material types, withstanding temperatures up to 109 ºC.

Good Surface Finish - Polymaker™ PC-ABS renders parts with a good surface finish and displays good surface adhesion which makes it easier to post process. Polymaker™ PC-ABS is well-suited for painting. bonding and specialized for surface finishings, i.e. by electroplating and metallization.

Formulated For 3D Printing - Using Covestro’s Bayblend® family as its base material, Polymaker™ PC-ABS is specifically engineered for 3D printing to combine excellent mechanical properties and printing quality. Bayblend® is a commonly used plastic in the automotive and information technology industry. Enclosure and 90°C heated bed required; a heated chamber is highly recommended.

Uncompromised Quality - Polymakers leading quality control process and rigorous in-house testing ensure reliable printing and consistency across spools and batches.

Find a reseller

Print Settings

Nozzle Temperature:
250˚C – 270˚C

Printing Speed:
30mm/s – 50mm/s

Bed Temperature:
90˚C – 105˚C

Chamber Temperature:
90˚C – 100˚C

Bed Surface:
Almost any surface with a thin coat of PVA glue

Cooling Fan:

Note: Based on 0.4 mm nozzle and Simplify 3D v.3.1. Printing conditions may vary with different printers and nozzle diameters

Mechanical Properties

Young’s Modulus:
1832 ± 65 (MPa)

Tensile Strength:
39.9 ± 1.0 (MPa)

Bending Strength:
66.3 ± 1.3 (MPa)

Charpy Impact Strength:
25.8 ± 1.4 (kJ/m2)


Thermal Properties

Glass Transition Temperature:

Vicat Softening Temperature:

Melting Temperature:



Recommended Support Materials:
PolyDissolve™ S2

When printing with Polymaker™ PC-ABS it is recommended to use a heated chamber.
It is recommended to anneal the printed part right after the printing process to release the residual internal stress when not using a heated chamber.

Annealing settings: 100˚C for 2h

Technical Data Sheets:
Contact your local reseller

Safety Data Sheets:
Contact your local reseller